Junyichem Co, LTD is located in Shanghai China. We are a research and production enterprise that serve the chemical industry.we have professional research and technical service team and are committed to become a manufacturer service provider with forward-looking research of new materials in chemical industry，贊南發動機襯墊氫化丁晴. Serve the rubber, plastic, coating，贊南發動機襯墊氫化丁晴，贊南發動機襯墊氫化丁晴, paint, ink and other industries. We have several production bases in China, our products include special additives, resins and functional reinforcing filler etc Junyichem provide special BETA functional additives, annual output of 3000 tons Junyichem provide BETA color master batches, annual output of 3000 tons Betachem provide quality AdvanZ resins annual output
目前能夠產業化生產HNBR的幾家公司均采用溶液法NBR催化加氫的工藝技術，具體工藝技術細節和工廠運行都屬于企業的商業機密，沒有公開的披露。但是有據可查的是各家所采用的加氫催化體系，瑞翁公司采用的是高活性、高選擇性的以二氧化硅為載體的非均相鈀系催化劑（Pd/SiO2），阿朗新科采用的是均相銠系催化體系，贊南科技則獨辟蹊徑，采用**的“詹氏催化劑”（釕系催化劑），成功解決了氫化丁腈橡膠工業化生產中的催化加氫活性、選擇性、產品后處理等關鍵技術問題，通過“詹氏催化劑”獨特的聚合物復分解加氫反應催化作用，有效地控制了HNBR生膠凝膠含量、分子量及分子量分布等直接影響膠料加工工藝性能的化學結構，開發出了不同門尼粘度（20-130）、不同丙烯腈含量（20-50 %）以及不同飽和度（氫化度80-99 %）的Zhanber® HNBR系列產品。
耐化學介質和耐臭氧性能
HNBR在高溫下能耐酸、堿和鹽，能在強性添加劑的潤滑油和燃料油介質中工作。在模擬油田深井開采酸性液/氣介質環境時（氣相：5％H2S、20％CO2、75％CH4，液相：95％柴油、4％水、1％緩蝕劑），由實驗曲線可以看出，FKM、TFE/P、NBR均不能承受高溫下的酸性介質環境，而HNBR表現出比較好性能。HNBR試樣的靜態和動態耐臭氧性能測試結果表明，1000小時后試樣未出現臭氧裂紋，顯示出優異的耐臭氧老化性能
耐寒性：通常丁腈橡膠中腈基含量越高，玻璃化溫度也越高，耐寒性變差。HNBR的玻璃化溫度除了受腈基含量影響外，還與碘值（氫化率）有關。當丙烯腈含量小于34％時，隨氫化率的增加，玻璃化溫度上升。而在腈基含量高時，隨著氫化率的增加，玻璃化溫度變化不明顯。由TR試驗結果（ASTM D1329）可見（圖5），當丙烯腈含量為34％時，隨著氫化率增加，TR10值增加，當丙烯腈含量超過40％時，隨著氫化率增加，TR10值降低。這種現象產生的原因在于HNBR的結晶化，近開發的耐寒性HNBR不但能抑止氫化引起玻璃化溫度上升，其耐熱性也得到改善。